≤nAtoms≤
≤nElements≤
Space Group:
≤ Gap ≤
≤ Dir. Gap ≤
≤ Met. ≤
Formula
Composition
(ν0,ν1ν2ν3)
Source ID

13628 materials founds

▹ Formula ▹ Source ▹ ID ▹ space group ▹ centered ▹ nat ▹ ne ▹ dim ▹ gap ▹ dir. gap ▹ met. ▴ ν wcc ▹ updated
RbScO2 COD 1528203 P6_3/mmc (194) ✔ 8 64 2 3.4955 3.922 0.000 (0;000) ✗ 27/01/17
RbTlO2 ICSD 33554 R-3m (166) ✔ 4 34 2 1.027 1.160 0.000 (0;000) ✗ 27/01/17
RbYO2 ICSD 49651 R-3m (166) ✔ 4 32 3 3.6441 3.794 0.000 (0;000) ✗ 27/01/17
ReO2 ICSD 154021 P4_2/mnm (136) ✔ 6 54 3 0.0 0.000 0.836 (0;000) ✗ 27/01/17
As2Os COD 9012561 Pnnm (58) ✔ 6 52 3 0.6395 1.158 0.000 (0;000) ✗ 05/01/17
Sr4As2O ICSD 33904 I4/mmm (139) ✔ 7 56 1 1.1057 1.131 0.000 (0;000) ✗ 05/01/17
RhO2 ICSD 647367 P4_2/mnm (136) ✔ 6 58 3 0.0 0.000 0.664 (0;000) ✗ 27/01/17
RuO2 ICSD 66939 Pa3 (205) ✔ 12 112 3 0.0 0.073 0.395 (0;000) ✗ 27/01/17
RuO2 COD 9007541 P4_2/mnm (136) ✔ 6 56 3 0.0 0.001 0.306 (0;000) ✗ 27/01/17
SbO2 COD 9005378 C2/c (15) ✔ 12 68 3 0.0 2.618 1.000 (0;000) ✗ 27/01/17
SiO2 ICSD 25632 Ibam (72) ✔ 6 32 1 2.7504 3.123 0.000 (0;000) ✗ 27/01/17
SiO2 COD 4124078 Fddd (70) ✔ 12 64 3 5.8964 5.896 0.000 (0;000) ✗ 27/01/17
SiO2 COD 4124079 P2/c (13) ✔ 12 64 3 0.4641 0.464 0.000 (0;000) ✗ 27/01/17
SiO2 COD 5910147 P6_3/mmc (194) ✔ 12 64 3 5.6701 5.670 0.000 (0;000) ✗ 27/01/17
SiO2 COD 9002782 Pbcn (60) ✔ 12 64 3 5.5934 5.593 0.000 (0;000) ✗ 27/01/17
SiO2 COD 9006291 C2/c (15) ✔ 12 64 3 5.825 5.862 0.000 (0;000) ✗ 27/01/17
SiO2 COD 9007154 P4_2/mnm (136) ✔ 6 32 3 6.8678 6.868 0.000 (0;000) ✗ 27/01/17
SiO2 COD 9008231 Fd-3m (227) ✔ 6 32 3 5.6616 5.663 0.000 (0;000) ✗ 27/01/17
SiO2 COD 9009218 Pa3 (205) ✔ 12 64 3 10.1731 10.473 0.000 (0;000) ✗ 27/01/17
SiO2 COD 9009238 P2_1/c (14) ✔ 18 96 3 5.5754 5.575 0.000 (0;000) ✗ 27/01/17
SnO2 ICSD 56677 Pa3 (205) ✔ 12 104 3 2.2532 2.319 0.000 (0;000) ✗ 27/01/17
SnO2 COD 1526637 P4_2/mnm (136) ✔ 6 52 3 1.1983 1.198 0.000 (0;000) ✗ 27/01/17
SrO2 COD 1100026 I4/mmm (139) ✔ 3 22 1 2.2477 2.248 0.000 (0;000) ✗ 27/01/17
Sc2SO2 ICSD 2450 P6_3/mmc (194) ✔ 10 80 3 1.9892 2.727 0.000 (0;000) ✗ 27/01/17
TaO2 ICSD 603572 P4_2/mnm (136) ✔ 6 50 3 0.0 0.000 0.903 (0;000) ✗ 27/01/17
TeO2 ICSD 647519 P4_2/mnm (136) ✔ 6 36 3 0.0 0.890 0.307 (0;000) ✗ 27/01/17
TiO2 ICSD 75179 Pnma (62) ✔ 12 96 3 2.5159 2.569 0.000 (0;000) ✗ 27/01/17
TiO2 COD 1511015 P4_2/mnm (136) ✔ 6 48 3 1.8907 1.891 0.000 (0;000) ✗ 27/01/17
TiO2 COD 1528778 C2/m (12) ✔ 12 96 3 2.9207 3.025 0.000 (0;000) ✗ 27/01/17
TiO2 COD 2310486 Pbcn (60) ✔ 12 96 3 2.5234 2.523 0.000 (0;000) ✗ 27/01/17
TiO2 COD 9007432 P4_2/mnm (136) ✔ 6 48 3 1.9813 1.981 0.000 (0;000) ✗ 27/01/17
TiO2 COD 9008216 I4_1/amd (141) ✔ 6 48 3 2.1406 2.472 0.000 (0;000) ✗ 27/01/17
TiO2 COD 9015355 P2_1/c (14) ✔ 12 96 3 1.2133 1.213 0.000 (0;000) ✗ 27/01/17
VO2 ICSD 51214 I4/m (87) ✔ 12 100 3 0.0 0.002 0.925 (0;000) ✗ 27/01/17
VO2 COD 4336391 P4_2/mnm (136) ✔ 6 50 3 0.0 0.000 0.875 (0;000) ✗ 27/01/17
As2Ru COD 9012558 Pnnm (58) ✔ 6 52 3 0.4005 1.052 0.000 (0;000) ✗ 05/01/17
CdC ICSD 183178 F-43m (216) ✗ 2 16 3 0.0 0.000 0.842 (0;000) ✔ 06/10/16
VO2 COD 9009089 P2_1/c (14) ✔ 12 100 3 0.0 0.009 0.453 (0;000) ✗ 27/01/17
KSb2 ICSD 80945 C2/m (12) ✔ 6 38 1 0.1801 0.569 0.000 (0;000) ✔ 02/02/17
ZrO2 ICSD 79915 Pnma (62) ✔ 12 64 3 2.7017 2.702 0.000 (0;000) ✗ 27/01/17
ZrO2 COD 1010912 P2_1/c (14) ✔ 12 64 3 2.3876 2.459 0.000 (0;000) ✗ 27/01/17
ZrO2 COD 1522143 P2_1/c (14) ✔ 12 64 3 3.4213 3.421 0.000 (0;000) ✗ 27/01/17
ZrO2 COD 1525705 P4_2/nmc (137) ✔ 6 32 3 2.5848 2.591 0.000 (0;000) ✗ 27/01/17
ZrO2 COD 1525707 Fm-3m (225) ✔ 3 16 3 2.8098 3.454 0.000 (0;000) ✗ 27/01/17
ZrO2 COD 1526427 P4_2/nmc (137) ✔ 6 32 3 3.4892 3.667 0.000 (0;000) ✗ 27/01/17
BiTeI ICSD 10500 P3m1 (156) ✗ 3 18 2 0.0 0.006 0.255 (0;000) ✔ 06/10/16
PbSeO3 COD 1526029 P2_1/m (11) ✔ 10 76 2 2.6043 2.604 0.000 (0;000) ✗ 27/01/17
PbSO3 COD 9009622 P2_1/m (11) ✔ 10 76 3 2.8374 2.837 0.000 (0;000) ✗ 27/01/17
TiPbO3 COD 9011193 Pm-3m (221) ✔ 5 44 3 1.6718 1.692 0.000 (0;000) ✗ 27/01/17
PdSeO3 ICSD 415955 C2/m (12) ✔ 10 84 2 0.6437 0.644 0.000 (0;000) ✗ 27/01/17